| Physical Properties and Durability |
Test Designation |
Fluropon® Coatings |
Flurothane® II Coatings |
Flurothane® IV Coatings |
| Dry Film Thickness (Minimum) |
ASTM D 4138 | 0.2 mils primer 0.7 mils topcoat |
1.0 mils 0.75 mils topcoat |
0.40 mils primer 1.0 mils primer 1.0 mils primer 0.75 topcoat |
| Specular Gloss Standard |
ASTM D 523@ 60º | 20-35 | 20 - 35 | 20-35 |
| Specular Gloss Low Gloss or Low Sheen |
ASIM D 523@ 85º | 5-15 | 5 - 15 | 5- 15 |
| Pencil Hardness | ASTM 0 3363 | HB - 2H | HB - 2H | HB - 2H |
| Flexibility T-Bend | ASTM D 4145 No adhesion loss |
2T No adhesion loss |
21 minimum No adhesion loss |
21 minimum No adhesion loss |
| Flexibility Mandrel 1/8' (3mm) - 180º Bend |
ASTM 0 522 | No cracking or adhesion loss |
No cracking or adhesion loss |
No cracking or adhesion loss |
| Cross Hatch Adhesion | ASTM D 3359 | No loss of adhesion | No loss of adhesion | No loss of adhesion |
| Reverse Impact | ASTM D 2794 | HDG (G-90) Galvalume: 3X Metal Thickness in inch-lbs No adhesion loss |
HDG (G-90) Galvalume: 3X Metal Thickness in inch-lbs No adhesion loss |
HDG (G-90) Galvalume: 3X Metal Thickness in inch-lbs No adhesion loss |
| Aluminum: 1.5X Metal Thickness in inch-lbs. No adhesion loss |
Aluminum: 1.5X Metal Thickness in inch-lbs. No adhesion loss |
Aluminum: 1.5X Metal Thickness in inch-lbs. No adhesion loss |
||
| Abrasion Resistance (Abrasion Coefficient) |
ASTM D 968 | 65 ± 10 liters Standard Gloss 100 ± 10 liters at 1.3 mil thickness |
100 ± 10 liters | 200 ± 20 liters Standard Gloss 315 ± 30 liters Low Gloss |
| Chemical Resistance | ASTM 0 1308 | 20% Sulfuric Acid - 18 Hrs. No visible change 25% Sodium Hydroxide - 1 Hr. No visible change 20% Muriatic Acid - 15 minutes No visible change |
20% Sulfuric Acid - 18 Hrs. No visible change 25% Sodium Hydroxide - 1 Hr. No visible change 20% Muriatic Acid - 15 minutes No visible change |
20% Sulfuric Acid - 18 Hrs. No visible change 25% Sodium Hydroxide - 1 Hr. No visible change 20% Muriatic Acid - 15 minutes No visible change |
| Flame Test | ASTM E 84 | Class A coating | Class A coating | Class A coating |
| Accelerated Weathering | ASTM D 3361 Dew Cycle Weatherometer 1000 Total Hours |
Color: 5ΔE Hunter units max. Chalk: Rating of 8 minimum |
Color: 51ΔE Hunter units max. Chalk: Rating of 8 minimum |
Color: 5ΔE Hunter units max. Chalk: Rating of 8 minimum |
| Outdoor Weathering South Florida Exposure 10 Years at 45º Angle |
ASTM D 2244 ASTM D 4214 |
Color: 5ΔE Hunter units max. Chalk: Rating of 8 minimum |
Color: 5ΔE Hunter units max. Chalk: Rating of 8 minimum |
Color: 5ΔE Hunter units max. Chalk: Rating of 8 minimum |
| Salt Spray | ASIM B 117 | HOG (G-90)/Galvalume: 1000 Hrs. Maximum of 1/16" (2mm) Creep from Scribe, No field blisters Aluminum: 3000 Hrs. No creep from scribe, No field blisters |
HOG (G-90)/Galvalume: 2000 Hrs. Maximum of 1/16" (2mm) Creep from Scribe, No field blisters Aluminum: 4000 Hrs. No creep from scribe, No field blisters |
HOG (G-90)/Galvalume: 2000 Hrs. Maximum of 1/32(1mm) Creep from Scribe, No field blisters Aluminum: 4000 Hrs. No creep from scribe, No field blisters |
| Humidity | ASTM 02247 | HDG (G-90) Galvalume: 2000 Hrs., No field blisters Aluminum: 3000 Hrs., No field blisters |
HDG (G-90) Galvalume: 3000 Hrs., No field blisters Aluminum: 4000 Hrs., No field blisters |
HDG (G-90) Galvalume: 4000 Hrs., No field blisters Aluminum: 4000 Hrs., No field blisters |
http://www.paintandcolor.com |
Fluropon, Flurothane and the Valspar logo are all registered trademarks of The Valspar Corporation. |